本帖最后由 邹阳 于 2012-7-9 22:55 编辑https://bbs.hcbbs.com/data/attachment/image/000/88/55/22_200_200.jpg
https://bbs.hcbbs.com/data/attachment/image/000/88/55/21_200_200.jpg
https://bbs.hcbbs.com/data/attachment/image/000/88/55/20_200_200.jpg
https://bbs.hcbbs.com/data/attachment/image/000/88/55/19_200_200.jpg
https://bbs.hcbbs.com/data/attachment/image/000/88/55/15_200_200.jpg
https://bbs.hcbbs.com/data/attachment/image/000/88/55/16_200_200.jpg
https://bbs.hcbbs.com/data/attachment/image/000/88/55/17_200_200.jpg
https://bbs.hcbbs.com/data/attachment/image/000/88/55/18_200_200.jpg
https://bbs.hcbbs.com/data/attachment/image/000/88/55/11_200_200.jpg
https://bbs.hcbbs.com/data/attachment/image/000/88/55/13_200_200.jpg
https://bbs.hcbbs.com/data/attachment/image/000/88/55/14_200_200.jpg
https://bbs.hcbbs.com/data/attachment/image/000/88/55/10_200_200.jpg
https://bbs.hcbbs.com/data/attachment/image/000/88/55/09_200_200.jpg
触媒颜色发绿，经过取样烘干后，还是绿色的。公司老员工说是触媒中毒了…… 你没烘到那个温度水应该烘不出来，看样子是受潮问题不应太大，只是上面隔板怎么会腐蚀呢，不是不锈钢的吗？ 业主是哪个单位？才多长时间？催化剂就这样。
双儿 发表于 2012-7-10 11:00
登录/注册后可看大图
你没烘到那个温度水应该烘不出来，看样子是受潮问题不应太大，只是上面隔板怎么会腐蚀呢，不是不锈钢的吗？
隔板的材质，不详。请问需要烘干多少度，才能烘干水分？
crygch 发表于 2012-7-10 23:30
登录/注册后可看大图
业主是哪个单位？才多长时间？催化剂就这样。
我是2010年9月份开车，有1年半，您能具体讲解一下吗?我们没有什么经验也看不出来什么。
邹阳 发表于 2012-7-15 09:49
登录/注册后可看大图
隔板的材质，不详。请问需要烘干多少度，才能烘干水分？
可以加热到500°C左右试试，时间维持长一点，看看情况怎么样。 貌似用真空抽吸来扒出催化剂的， 不知效果如何？
床层里露出来的是热电偶吗？安装的位置似乎不理想，上下固定在一起就更不好了。
boqing_zh 发表于 2012-7-15 10:07
登录/注册后可看大图
貌似用真空抽吸来扒出催化剂的， 不知效果如何？
床层里露出来的是热电偶吗？安装的位置似乎不理想，上下 ...
是用真空抽的。这个技术是从三门峡中原冶炼厂学来的
邹阳 发表于 2012-7-15 09:49
登录/注册后可看大图
隔板的材质，不详。请问需要烘干多少度，才能烘干水分？
按照高温吹气的温度应大于400度，一般没问题，我们在高温吹气时，一般只能保证一段和四段，如果吹气后还含有少量的二氧化硫，打开后一般会发绿，最好查一下活性，如果五氧化钒的含量不低于6%应还能用的。